Azzar reżistenti għas-sħana kkastjar EN10295
Il-kumpanija tagħna tipproduċi azzar reżistenti għas-sħana f'konformità mal-istandards Ewropej, tipprovdi customization tal-ipproċessar, merħba tixtri
Proprjetajiet mekkaniċi attemperatura tal-kamra
|
Denominazzjoni |
Saħħan trattament |
Tensili Test |
Ebusija HB massimu. |
||||||
|
Simbolu |
Temperatura grad |
Fpo,2 Mpa a min. |
Rm Mpa a min. |
A % min. |
|||||
|
Isem |
Numru |
||||||||
|
Ferritiċi u awstenitiċi - gradi ferritiċi |
GX30CrSiz b |
1.4710 |
+ AC |
800 sa 850 |
300 |
||||
|
GX40CrSi13 |
1.4729 |
+ AC |
800 sa 850 |
300 |
|||||
|
GX40CrSi17 |
1.4740 |
+ AC |
800 sa 850 |
300 |
|||||
|
GX40CrSi24 |
1.4745 |
Nru sħana trattament |
d |
||||||
|
GX40CrSi28 |
1.4776 |
d |
|||||||
|
GX130CrSi29 |
1.4777 |
d |
|||||||
|
GX160CrSi18 |
1.4743 |
d |
|||||||
|
GX40CrNiSi27-4 |
1.4823 |
250 |
550 |
3 |
d |
||||
|
Gradi awstenitiċi |
GX25CrNiSi18-9 |
1.4825 |
230 |
450 |
15 |
||||
|
GX40CrNiSi22-10 |
1.4826 |
230 |
450 |
8 |
|||||
|
GX25CrNiSi20-14 |
1.4832 |
230 |
450 |
10 |
|||||
|
GX40CrNiSi25-12 |
1.4837 |
220 |
450 |
6 |
|||||
|
GX40CrNiSi25-20 |
1.4848 |
220 |
450 |
8 |
|||||
|
GX40CrNiSiNb24-24 |
1.4855 |
220 |
450 |
4 |
|||||
|
GX35NiCrSi25-21 |
1.4805 |
220 |
430 |
8 |
|||||
|
GX40NiCrSi35-17 |
1.4806 |
220 |
420 |
6 |
|||||
|
GX40NiCrSiNb35-18 |
1.4807 |
220 |
420 |
4 |
|||||
|
GX40NiCrSi38-19 |
1.4865 |
220 |
420 |
6 |
|||||
|
GX40NiCrSiNb38-19 |
1.4849 |
220 |
420 |
4 |
|||||
|
GX10NiCrSiNb32-20 |
1.4859 |
180 |
440 |
20 |
|||||
|
GX40NiCrSi35-26 |
1.4857 |
220 |
440 |
6 |
|||||
|
GX40NiCrSiNb35-26 |
1.4852 |
220 |
440 |
4 |
|||||
|
GX50NiCrCo20-20-20 |
1.4874 |
320 |
420 |
6 |
|||||
|
GX50NiCrCoW35-25- 15-5 |
1.4869 |
270 |
480 |
5 |
|||||
|
GX40NiCrNb45-35 |
1.4889 |
240 |
440 |
3 |
|||||
|
Nikil u kobalt |
ligi bażi |
G-NiCr28W |
2.4879 |
240 |
440 |
3 |
|||
|
G -CoCr28 |
2.4778 |
235 |
490 |
6 |
|||||
|
G-NiCr50Nb |
2.4680 |
230 |
540 |
8 |
|||||
|
G-NiCr15 |
2.4815 |
200 |
400 |
3 |
|||||
|
a 1MPa=1 N/mm2 b Jekk dan il-grad jintuża għal kkastjar reżistenti għall-ilbies, allura jistgħu jiġu kkunsinnati mingħajr trattament bis-sħana. c + A tfisser: Ittemprar d L-ikkastjar jistgħu jiġu forniti wkoll fil-kondizzjoni ittemprat f'liema każ jista' jiġi miftiehem valur massimu ta' ebusija. |
|||||||||